Method of manufacturing a composite golf club head

ABSTRACT

A method for manufacturing a golf club head with a face component composed of a plurality of plies of pre-preg material and having a striking plate portion with a thickness in the range of 0.010 to 0.250 inches is disclosed herein. The golf club also has a crown component composed of a plurality of plies of pre-preg material and a sole component composed of a plurality of plies of pre-preg material. The golf club head is manufactured using a bladder compression molding process.

CROSS REFERENCES TO RELATED APPLICATIONS

[0001] This application is a continuation-in-part application of co-pending U.S. patent application Ser. No. 09/877,652, filed on Jun. 8, 2001, which is a continuation of U.S. patent application Ser. No. 09/474,670, filed on Dec. 29, 1999, now U.S. Pat. No. 6,248,025, which is continuation-in-part application of U.S. patent application Ser. No. 08/958,723, filed on Oct. 23, 1997, now U.S. Pat. No. 6,010,411.

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT

[0002] Not Applicable

BACKGROUND OF THE INVENTION

[0003] 1. Field of the Invention

[0004] The present invention relates to a manufacturing method for a golf club head composed of plies of pre-preg sheets. More specifically, the present invention relates to a bladder-mold manufacturing method for a golf club head composed of plies of pre-preg sheets.

[0005] 2. Description of the Related Art

[0006] One of the first (if not the first) disclosures of a golf club head composed of a plurality of plies of a pre-preg material is Great Britain Patent Application Number 1201648 which was filed in 1967 on behalf of William Charles Carlton.

[0007] In 1984, U.S. Pat. No. 4,449,707 issued to Hayashi et al., for a Golf Club Head Of Carbon Fiber Reinforced Plastic, based on a Japanese Patent Application originally filed in 1982. The Hayashi Patent discloses surrounding a core with a fiber reinforced fabric to create a golf club head with a proper center of gravity.

[0008] Another disclosure is U.S. Pat. No. 4,545,580 to Tomita et al., for a Wood-Type Golf Club Head, based on a Japanese Patent Application originally filed in 1983. The Tomita Patent discloses a durable golf club head having an outer shell composed of a fiber reinforced plastic material, a foam center core, and an intermediate shell formed of a thermoplastic resin material.

[0009] Yet another disclosure is U.S. Pat. No. 4,630,826 to Nishigaki et al., for Golf Club Head. The Nishigaki Patent discloses body composed of a carbon resin layer and a cast resin layer with a face insert block composed of a ceramic material.

[0010] Still another disclosure is U.S. Pat. No. 4,778,185 to Kurokawa, for Wood-Type Core-Shell Golf Club Heads, based on a Japanese Patent Application originally filed in 1984. The Kurokawa Patent discloses a golf club head composed of a foam core and a shell composed of a material fiber reinforced plastic having long and short fibers.

[0011] Yet another disclosure is U.S. Pat. No. 4,793,616 to Fernandez, for Golf Club. The Fernandez Patent discloses a club head shell composed resin impregnated fibers and ceramic particles within the resin to provide a high strength shell.

[0012] Yet another disclosure is U.S. Pat. No. 5,154,425 to Niskanen et al., for a Composite Golf Club Head. The Niskanen Patent discloses a club head composed of a metal matrix composite of a ceramic matrix composite.

[0013] When a golf club head strikes a golf ball, large impacts are produced that load the club head face and the golf ball. Most of the energy is transferred from the head to the golf ball, however, some energy is lost as a result of the collision. The golf ball is typically composed of polymer cover materials (such as ionomers) surrounding a rubber-like core. These softer polymer materials having damping (loss) properties that are strain and strain rate dependent which are on the order of 10-100 times larger than the damping properties of a metallic club striking plate. Thus, during impact most of the energy is lost as a result of the high stresses and deformations of the golf ball (0.001 to 0.20 inches), as opposed to the small deformations of the metallic club face (0.025 to 0.050 inches). A more efficient energy transfer from the club head to the golf ball could lead to greater flight distances of the golf ball.

[0014] The generally accepted approach has been to increase the stiffness of the club head face to reduce metal or club head deformations. However, this leads to greater deformations in the golf ball, and thus increases in the energy transfer problem.

[0015] Some have recognized the problem and disclosed possible solutions. An example is Campau, U.S. Pat. No. 4,398,965, for a Method Of Making Iron Golf Clubs With Flexible Impact Surface, which discloses a club having a flexible and resilient face plate with a slot to allow for the flexing of the face plate. The face plate of Campau is composed of a ferrous material, such as stainless steel, and has a thickness in the range of 0.1 inches to 0.125 inches.

[0016] Another example is Eggiman, U.S. Pat. No. 5,863,261, for a Golf Club Head With Elastically Deforming Face And Back Plates, which discloses the use of a plurality of plates that act in concert to create a spring-like effect on a golf ball during impact. A fluid is disposed between at least two of the plates to act as a viscous coupler.

[0017] Yet another example is Jepson et al, U.S. Pat. No. 3,937,474, for a golf Club With A Polyurethane Insert. Jepson discloses that the polyurethane insert has a hardness between 40 and 75 shore D.

[0018] Still another example is Inamori, U.S. Pat. No. 3,975,023, for a Golf Club Head With Ceramic Face Plate, which discloses using a face plate composed of a ceramic material having a high energy transfer coefficient, although ceramics are usually harder materials. Chen et al., U.S. Pat. No. 5,743,813 for a Golf Club Head, discloses using multiple layers in the face to absorb the shock of the golf ball. One of the materials is a non-metal material.

[0019] Lu, U.S. Pat. No. 5,499,814, for a Hollow Club Head With Deflecting Insert Face Plate, discloses a reinforcing element composed of a plastic or aluminum alloy that allows for minor deflecting of the face plate which has a thickness ranging from 0.01 to 0.30 inches for a variety of materials including stainless steel, titanium, KEVLAR®, and the like. Yet another Campau invention, U.S. Pat. No. 3,989,248, for a Golf Club Having Insert Capable Of Elastic Flexing, discloses a wood club composed of wood with a metal insert.

[0020] The Rules of Golf, established and interpreted by the United States Golf Association (“USGA”) and The Royal and Ancient Golf Club of Saint Andrews, set forth certain requirements for a golf club head. The requirements for a golf club head are found in Rule 4 and Appendix II. A complete description of the Rules of Golf are available on the USGA web page at www.usga.org. Although the Rules of Golf do not expressly state specific parameters for a golf club face, Rule 4-1e prohibits the face from having the effect at impact of a spring with a golf ball. In 1998, the USGA adopted a test procedure pursuant to Rule 4-1e which measures club face COR. This USGA test procedure, as well as procedures like it, may be used to measure club face COR.

[0021] Although the prior art has disclosed many club head composed of composite materials, the prior art has failed to provide a golf club head composed of a composite material that is lightweight, forgiving and has a high coefficient of restitution.

BRIEF SUMMARY OF THE INVENTION

[0022] The present invention provides a method for manufacturing a golf club head that is composed of a composite material and is forgiving while providing better performance than other composite golf club heads.

[0023] One aspect of the present invention is a method for producing a golf club head composed of plies of pre-preg sheets. The method begins with creating a face component composed of plies of pre-preg sheets. Next, a crown component composed of plies of pre-preg sheets is created and a sole component composed of plies of pre-preg sheets is created using the method. Next, the face component, the crown component and the sole component are assembled to create an assembled unit with an inflatable bladder within a hollow interior of the assembled unit. Next, the assembled unit is pre-compacted to create a pre-compacted unit. Finally, the pre-compacted unit is bladder molded to create a molded golf club head.

[0024] Having briefly described the present invention, the above and further objects, features and advantages thereof will be recognized by those skilled in the pertinent art from the following detailed description of the invention when taken in conjunction with the accompanying drawings.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

[0025]FIG. 1 is an exploded view of a golf club head manufactured by the method of the present invention.

[0026]FIG. 2 is a front view of a golf club head manufactured by the method of the present invention.

[0027]FIG. 2A is a front view of a golf club head manufactured by the method of the present invention.

[0028]FIG. 3 is a top plan view of a golf club head manufactured by the method of the present invention.

[0029]FIG. 4 is a heel end view of a golf club head manufactured by the method of the present invention.

[0030]FIG. 5 is a toe end view of a golf club head manufactured by the method of the present invention.

[0031]FIG. 6 is a bottom plan view of a golf club head manufactured by the method of the present invention.

[0032]FIG. 7 is a cross-sectional view of the golf club head of FIG. 3 along line 7-7.

[0033]FIG. 8 is a cross-sectional view of the golf club head of FIG. 2 along line 8-8.

[0034]FIG. 9 is an isolated cross-section view of a face preform of the present invention.

[0035]FIG. 9A is an enlarged view of area A of FIG. 9.

[0036]FIG. 9B is an enlarged view of area B of FIG. 9.

[0037]FIG. 10 is an isolated cross-section view of a crown/face preform of a golf club head of the present invention.

[0038]FIG. 11 is an isolated cross-section view of a sole preform of the present invention.

[0039]FIG. 12 is a top plan view of a golf club head manufactured by the method of the present invention illustrating the variation in thickness of the walls of the golf club head.

[0040]FIG. 13 is a front plan view of a golf club head manufactured by the method of the present invention illustrating the variation in thickness of the walls of the golf club head.

[0041]FIG. 14 is a bottom plan view of a golf club head manufactured by the method of the present invention illustrating the variation in thickness of the walls of the golf club head.

[0042]FIG. 15 is a heel end view of a golf club head manufactured by the method of the present invention illustrating the variation in thickness of the walls of the golf club head.

[0043]FIG. 16 is a plan view of a face/crown ply having a ninety degree orientation.

[0044]FIG. 17 is a plan view of a full face ply having a ninety degree orientation.

[0045]FIG. 18 is a plan view of a face doubler ply having a ninety degree orientation.

[0046]FIG. 19 is a plan view of a sole ply having a negative forty-five degree orientation.

[0047]FIG. 20 is a flow chart of the general method of the present invention.

[0048]FIG. 21 is a flow chart of the face component creation step of the method of the present invention.

[0049]FIG. 22 is a flow chart of the compressing molding step of the method of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

[0050] The present invention is directed at a method of manufacturing a golf club head that has a large volume and a minimum mass. The golf club head is forgiving and has a high coefficient of restitution thereby enabling for less dispersion and greater distance of a golf ball hit with the golf club of the present invention.

[0051] As shown in FIGS. 1-6, a golf club head is generally designated 20. The club head 20 is either a fairway wood or a driver. The drivers range in loft angle of from six degrees to fifteen degrees. The club head 20 has a body 22 that is generally composed of a composite material such as plies of carbon pre-preg sheets. The body 22 has a crown 24, a striking plate 26, a sole 28 with a bottom portion 28 a and a ribbon 30. The ribbon preferably has an upper ribbon wall 30 a and a lower ribbon wall 30 b. The ribbon 30 generally extends from a toe end 32 to a heel end 34. The ribbon 30 generally begins at one end of the striking plate 26 and ends at an opposite end of the striking plate 26. A rear 36 of the body 22 is opposite the striking plate 26 and is defined by portions of the ribbon 30, the crown 24 and the sole 28. Also, at the heel end 34 of the club head 20 is an internal tube 38 with an opening 39 for placement of a shaft therein. The internal tube 38 is placed within the hollow interior 44 of the body 22. Within the ribbon is a weight member 40.

[0052] A sole plate 42 is disposed within a recess 29 of the bottom portion 28 a of the sole 28. The sole plate 42 is preferably composed of a metal material such as aluminum or titanium, and preferably has a mass of 5 grams to 20 grams. A preferred mass for an aluminum sole plate 42 is approximately 11 grams, and a preferred mass for a titanium sole plate 42 is approximately 18 grams. The sole plate 42 is preferably bonded within the recess 29 through use of adhesives. The sole plate 42 preferably has embossed graphics thereon. The sole plate 42 increases the durability of the club head 20 since the sole 28 often impacts the ground during the striking of a golf ball.

[0053] The club head 20 also has a greater volume than a composite club head of the prior art while maintaining a weight that is substantially lower or equivalent to that of the prior art. The volume of the club head 20 ranges from 175 cubic centimeters to 450 cubic centimeters, more preferably ranges from 300 cubic centimeters to 400 cubic centimeters, and is most preferably 360 cubic centimeters for a driver. The mass of the club head 20 ranges from 165 grams to 300 grams, preferably ranges from 175 grams to 225 grams, and most preferably from 188 grams to 195 grams. The body 22 of plies of pre-preg material has a mass ranging from 80 grams to 120 grams, and most preferably 98 grams.

[0054] The volume of the golf club head 20 is increased by increasing the vertical distance of the club head 20 from the sole 28 to the crown 24, as opposed to the horizontal distance of the heel end 34 to the toe end 32. This increase in volume is brought about by the dual wall structure of the ribbon 30. The upper ribbon wall 30 a is approximately perpendicular relative to the crown 24, while the lower ribbon wall 30 b preferably has angle between 25 degrees to 75 degrees relative to the crown 24. The greater volume of the club head 20 allows the club head 20 to be more forgiving than prior art golf club heads while providing better performance. The mass of club head 20 is much lower than metal club heads of similar volumes, and thus the large volume does not deter from the swing of a golfer.

[0055] The striking plate 26 has a smaller aspect ratio than striking plates of the prior art. The aspect ratio as used herein is defined as the width, “w”, of the striking plate divided by the height, “h”, of the striking plate 26, as shown in FIG. 2A. In one embodiment, the width w is 90 millimeters and the height h is 54 millimeters giving an aspect ratio of 1.666. In conventional golf club heads, the aspect ratio is usually much greater than 1. For example, the original GREAT BIG BERTHA® driver had an aspect ratio of 1.9. The aspect ratio of the present invention preferably ranges from 1.0 to 1.7.

[0056] As shown in FIG. 7, the internal tube 38 lies within the hollow interior 44 of the club head 20. The internal tube is preferably composed of a metal material and has a mass ranging from 8 grams to 20 grams. The internal tube 38 is most preferably composed of stainless steel and has a mass of approximately 14 grams. The internal tubing 38 has a bore 130 to receive an insert and a shaft, not shown, therein. Such an insert is discussed in co-pending U.S. patent application Ser. No. 09/652,491, filed on Aug. 31, 2000, for a golf Club With Hosel Liner, which is hereby incorporated by reference in its entirety. Preferably, the club head 20 has a hollow interior 44 defined by the body 22, however, the light weight of the composite body 22 allows for numerous manipulations in placement of weight, foam, sound enhancing devices and the like within the hollow interior 44.

[0057] Referring specifically to FIG. 1, the club head 20 has a weight member 40 disposed within the plies of pre-preg that compose the ribbon 30 of the club head 20. Preferably, the weight member 40 is composed of three weight members 40 a, 40 b and 40 c. One such weight member 40 is described in co-pending U.S. patent application Ser. No. 09/474,688, filed on Dec. 29, 1999, and entitled A Composite Golf Club Head With An Integral Weight Strip, which is hereby incorporated by reference in its entirety. Another such weighting method is described in co-pending U.S. patent application Ser. No. 09/______, for Internal Weighting For A Composite Golf Club Head, filed on an even date herewith, and hereby incorporated by reference in its entirety. The weight member 40 has a mass ranging from 30 grams to 80 grams, more preferably 45 grams to 70 grams, and most preferably 54 grams. The weight member 40 is preferably composed of a polymer material integrated with a metal material. The metal material is preferably selected from copper, tungsten, steel, aluminum, tin, silver, gold, platinum, or the like. A preferred metal is tungsten. The weight member 40 has a density greater than the composite material of the body 22. Preferably, the weight member 40 extends from approximately the heel end 34 of the striking plate 26 through the rear 36 to the toe end 32 of the striking plate 26. However, the weight member 40 may only extend along the rear 36 of the ribbon 30, the heel end 34 of the ribbon 30, the toe end 32 of the ribbon 30, or any combination thereof. Those skilled in the pertinent art will recognize that other weighting materials may be utilized without departing from the scope and spirit of the present invention.

[0058] The placement of the weighting members 40 a-c allows for the moment of inertia of the golf club head 20 to be optimized. A more thorough description of the optimization of the moments of inertia is disclosed in co-pending U.S. patent application Ser. No. 09/796,951, filed on Feb. 27, 2001, entitled High Moment of Inertia Composite Golf Club, and hereby incorporated by reference in its entirety. In one preferred example of the golf club head 20 of the present invention, the moment of inertia about the Ixx axis through the center of gravity is approximately 2566 grams-centimeters squared (“g-cm²”), the moment of inertia about the Iyy axis through the center of gravity is approximately 1895 g-cm², and the moment of inertia about the Izz axis through the center of gravity is approximately 3368 g-cm².

[0059] As shown in FIGS. 8, 9, 9A and 9B, a return portion 100 is a transition area from a perimeter 29 of the striking plate 26 rearward towards the crown 24. The return portion 100 has a thickness ranging from 0.100 inch to 0.200 inch to control the compliance of the striking plate 26. The return portion 100 has an upper section 100 a, a lower section 100 b, a heel section 100 c, not shown, and a toe section 100 d, not shown. The return portion 100 also has a taper region 101, which includes an upper tapering region 101 a, a lower tapering region 101 b, a heel tapering region 101 c, not shown, and a toe tapering region 101 d, not shown. The tapering region 101 tapers in thickness from a greater thickness nearer the striking plate portion 26 to a lesser thickness rearward toward the crown 24.

[0060] The return portion 100 has a predetermined length which extends rearward from the perimeter 29 of the striking plate portion 26 into the crown 24. Preferably, the distance of the return portion 100, “Dr”, ranges from 0.25 inch to 2.0 inches, more preferably from 0.5 inch to 1.75 inches, and most preferably 1.5 inches. Preferably, the distance from the perimeter 29 to the beginning of the tapering region 101 of the return portion 100 ranges from 0.25 inch to 1.5 inches, and most preferably 1.0 inch.

[0061] The body 22 is manufactured from a face component 125, which includes the striking plate portion 26 and the return portion 100, a crown component 124 and a sole component 128. The crown component 124 overlaps the face component 125, as shown in FIG. 10. The sole component 128 includes the ribbon portion 30 and the bottom portion 28 a. The sole component 128 is attached to the crown component 124 and the face component 125.

[0062] FIGS. 16-19 illustrate preferred pre-preg sheets for forming the composite body of the golf club head 20. FIG. 16 illustrates a face/crown ply pre-preg sheet that is generally designated 55. The face/crown ply 55 has a plurality of fibers 51 dispersed within a resin body 53. The fibers 51 are preferably composed of a carbon material. Alternatively, the fibers 51 may be aramid fibers, glass fibers or the like. The resin is typically an epoxy material. The relation of the fibers 51 to the striking plate 26, when the striking plate 26 is in a position to strike a golf ball, determines the orientation of the fibers 51. If the fibers 51 are parallel with the ground, or in other words extending across from the toe end to the heel end, then the face/crown ply 55 has a zero degree orientation. If the fibers 51 are approximately perpendicular to the ground, as shown in FIG. 16, or in other words extending from the crown to the sole, then the face/crown ply 55 has a ninety degrees orientation.

[0063]FIG. 17 illustrates a full face ply pre-preg sheet that is generally designated 57. As with the face/crown ply 55, the full face ply 57 has a plurality of fibers 51 dispersed within a resin body 53. The fibers 51 extend from the sole 28 to the crown 24, and thus the full face ply 57 has fibers 51 that are perpendicular to the ground when it is in a position for striking a golf ball. Therefore, the full face ply 57 of FIG. 17 has a ninety degrees orientation.

[0064]FIG. 18 illustrates a face doubler ply pre-preg sheet that is generally designated 58. As with the face/crown ply 55, the face doubler ply 58 has a plurality of fibers 51 dispersed within a resin body 53. The fibers 51 extend from the sole 28 to the crown 24, and thus the face doubler ply 58 has fibers 51 that are perpendicular to the ground when it is in a position for striking a golf ball. Therefore, the face doubler ply 58 of FIG. 18 has a ninety degrees orientation.

[0065]FIG. 19 illustrates a sole ply pre-preg sheet that is generally designated 59. As with the face/crown ply 55, the sole ply 59 has a plurality of fibers 51 dispersed within a resin body 53. The fibers 51 extend at a forty-five degree angle relative to the ground when it is in a position for striking a golf ball. Therefore, the sole ply 59 of FIG. 19 has a forty-five degree orientation.

[0066] As previously stated, the preferred composite material is plies of carbon pre-peg sheets. Plies of pre-preg composite sheets are manufactured by pulling strands of fiber in a parallel motion, preferably carbon, aramid or glass fiber, through a resin film and allowing the resin to partially cure or “stage”. When the resin is partially staged, the resin holds the fibers together such that the fibers form a malleable sheet with all of the fibers in a specific orientation relative to an edge of the sheet. Preferred orientations are zero degrees, plus forty-five degrees, minus forty-five degrees and ninety degrees. Exemplary carbon pre-preg fiber sheets may be obtained from Newport Composites of Santa Ana, California, Fiberite Inc. of Greenville, Texas, or Hexcel Inc. of Pleasonton, Calif.

[0067] The manipulation of the thickness of the various regions of the body 22 allows the golf club head 20 to have superior durability, forgiveness and performance as compared to prior art composite golf club heads. As shown in FIGS. 12-15, the thickness of the body 22 is focused on the striking plate portion 26. In a most preferred example: the region designated A of the striking plate portion 26 has a thickness of approximately 0.169 inch; the region designated B, at the junction of the crown 24 and striking plate 26 has a thickness of approximately 0.188 inch; the region designated C of the bottom portion 28 a of the sole 28 has a thickness of approximately 0.221 inch; the region designated D of the ribbon 30 and of the bottom portion 28 a has a thickness of approximately 0.202 inch; the region designated E of the crown 24, the bottom portion 28 a and the ribbon 30 has a thickness of approximately 0.033 inch; and the region designated F of the crown 24 has a thickness of approximately 0.191 inch. The regions designated Z1, Z2, Z3, Z4, Z5 and Z6 are tapering zones where the thickness tapers rearward.

[0068] The golf club head 20 is preferably manufactured using a bladder molding process. One such process is described in U.S. Pat. No. 6,248,025, which is hereby incorporated by reference.

[0069]FIG. 20 illustrates the general method of the present invention. At block 200, the face component 125 or face cup preform is created by laying up a plurality of plies of pre-preg sheets. The plies of pre-preg sheets create the striking plate 26 and the return portion 100 of the face component 125. A detailed example of the face component 125 is set forth below. At block 202, the crown component 124 or crown preform is created by laying up a plurality of plies of pre-preg sheets over the face component 125 as shown in FIG. 10. The plies of pre-preg sheets create the crown 24, the striking plate 26 and the return portion 100. A detailed example of the crown component 124 is set forth below. At block 204, the sole component 128 or sole preform is created by laying up a plurality of plies of pre-preg sheets with a plurality of weight members 40 a-c. The plies of pre-preg sheets are folded over the plurality of weight members 40 a-c. The plies of pre-preg sheets create the ribbon 30 and the bottom portion 28 a. A detailed example of the sole component 128 is set forth below.

[0070] At block 206, the face cup component 125, crown component 124 and sole component 128 are assembled to form an assembled unit. An inflatable bladder, preferably made from latex, silicone, or similar materials, is placed within the interior of the assembled unit during assembly and an access end of the bladder is placed through the bladder port. At block 208, the assembled unit is placed within a compaction device and pre-compacted to form a pre-compacted unit. At block 210, the pre-compacted unit is placed within a compression mold for bladder molding of the pre-compacted unit into a molded unfinished golf club head. At block 212, the molded golf club head is finished to create the golf club head 20.

[0071] During the bladder molding, a source of pressurized gas (not shown) is attached by a gas line to the bladder, and the bladder is inflated within the hollow interior of the pre-compacted unit. The bladder engages the inside surface of the pre-compacted unit, forcing the plies of pre-preg sheets against the inner wall of the compression mold. The mold is then heated at a predetermined temperature for a selected period of time, i.e., a time sufficient to allow proper curing of the resin within the pre-preg sheets. After depressurizing, the bladder is removed through the bladder port 43, and the molded unfinished golf club head is removed from the compression mold. Those skilled in the art will appreciate that, depending upon the type of resin used, curing temperatures may range from 250° to 800° F., the requisite curing time may range from a few minutes (for example, in the case of a “quick cure” epoxy or a thermoplastic resin) to 1.5 hours, and the pressure applied via the latex or silicone bladder may range from 100 to 300 psi.

[0072]FIG. 21 illustrates the face component creation process of block 200 of FIG. 20. At block 300, a first predetermined quantity of plies of pre-preg sheets for the face component 125 are placed within a cavity configured to approximate the face component 125. At block 302, this first predetermined quantity of plies of pre-preg sheets for the face component 125 are compressed by using a plunger or other similar device to create a stack of compressed plies. At block 304, a second predetermined quantity of plies of pre-preg sheets for the face component 125 are placed within the cavity over the compressed plies. At block 306, this second predetermined quantity of plies of pre-preg sheets for the face component 125 are compressed by using a plunger or other similar device to create a stack of more compressed plies. At block 308, the process is repeated until a desired thickness of the face component 125 is achieved by the process.

[0073]FIG. 22 is a flow chart of the assembly and pre-compaction steps. At block 400, the face-component/crown component is created by laying up the plies of the crown component over the face component 125. At block 402, the inflatable bladder is placed within the sole component 128 and extended through the bladder port 43. At block 404, the assembled unit is placed within a compaction mold, and an extension of the bladder is extended through a bore in the mold. At block 406, the compaction mold is sealed and the assembled unit is compacted to form the pre-compaction unit.

[0074] In a preferred embodiment, the face component 125 is composed of forty-eight plies of pre preg sheets: forty full face plies 57 in orientations of zero degrees, plus forty-five degrees, minus forty-five degrees and ninety degrees; and eight face doubler plies 58 in zero degrees and ninety degrees orientations. The crown component 124, which is applied over the face component 125, is composed of seven face/crown plies 55 in orientations of zero degrees, plus forty-five degrees, minus forty-five degrees and ninety degrees. The sole component 128 is composed of seven sole plies 59 in orientations of zero degrees, plus forty-five degrees, minus forty-five degrees and ninety degrees. The second and third pairs of sole plies 59 are folded over the plurality of weight members 40 a-c. In this preferred embodiment, the outer plies are a twill pattern for aesthetic purposes and some durability support.

[0075] From the foregoing it is believed that those skilled in the pertinent art will recognize the meritorious advancement of this invention and will readily understand that while the present invention has been described in association with a preferred embodiment thereof, and other embodiments illustrated in the accompanying drawings, numerous changes, modifications and substitutions of equivalents may be made therein without departing from the spirit and scope of this invention which is intended to be unlimited by the foregoing except as may appear in the following appended claims. Therefore, the embodiments of the invention in which an exclusive property or privilege is claimed are defined in the following appended claims. 

We claim as our invention:
 1. A method for producing a golf club head composed of plies of pre-preg sheets, the method comprising: creating a face component composed of plies of pre-preg sheets, the face component having a striking plate portion and a return portion; creating a crown component composed of plies of pre-preg sheets; creating a sole component composed of plies of pre-preg sheets, the sole component having a ribbon and a bottom portion; assembling the face component, the crown component and the sole component to create an assembled unit with an inflatable bladder within a hollow interior of the assembled unit; pre-compacting the assembled unit to create a pre-compacted unit; and bladder molding the pre-compacted unit to create a molded golf club head.
 2. The method according to claim 1 wherein the face component is composed of 20 to 70 plies of pre-preg sheets.
 3. The method according to claim 1 wherein the sole component is composed of 4 to 20 plies of pre-preg sheets and a plurality of weighting members.
 4. The method according to claim 1 wherein the crown component is composed of 4 to 20 plies of pre-preg sheets.
 5. The method according to claim 1 wherein the club head has a volume ranging from 175 cubic centimeters to 600 cubic centimeters. 